Mécanismes de déformation et résistance à la rupture des polycristaux à grains ultra-fins études expérimentales et numériques by Lukasz Farbaniec( )

2 editions published in 2012 in French and held by 4 WorldCat member libraries worldwide

The objective of this thesis is to provide insights of two fundamental topics regarding the deformation and failure mechanisms of ultrafine-grained face-centered cubic metals. The first topic considers the mechanisms of plastic deformation as a desired grain fragmentation process in order to achieve a significant refinement of structural elements. For this purpose, the so-called Dynamic Plastic Deformation technique is used to cause the grain refinement of polycrystalline nickel. Subsequently, a Fast Fourier Transform numerical procedure is applied to the microstructure after deformation, and the results are compared with the experiments. The second topic deals with the effect of the stress state on ductile toughness along with identification of the mechanisms leading to tensile failure. To this end, a small-scale experimental and numerical modelling techniques are developed and implemented to predict fracture behaviour of polycrystalline nickel and steel. Consequently, the obtained results are used to formulate a criterion applied to the crack tip situation. The numerical results are compared with the experimental data to validate the procedure and estimate fracture toughness of the investigated material
Mécanismes de déformation et résistance à la rupture des polycristaux à grains ultra-fins : études expérimentales et numériques by Lukasz Farbaniec( Book )

2 editions published in 2012 in French and held by 3 WorldCat member libraries worldwide

The objective of this thesis is to provide insights of two fundamental topics regarding the deformation and failure mechanisms of ultrafine-grained face-centered cubic metals. The first topic considers the mechanisms of plastic deformation as a desired grain fragmentation process in order to achieve a significant refinement of structural elements. For this purpose, the so-called Dynamic Plastic Deformation technique is used to cause the grain refinement of polycrystalline nickel. Subsequently, a Fast Fourier Transform numerical procedure is applied to the microstructure after deformation, and the results are compared with the experiments. The second topic deals with the effect of the stress state on ductile toughness along with identification of the mechanisms leading to tensile failure. To this end, a small-scale experimental and numerical modelling techniques are developed and implemented to predict fracture behaviour of polycrystalline nickel and steel. Consequently, the obtained results are used to formulate a criterion applied to the crack tip situation. The numerical results are compared with the experimental data to validate the procedure and estimate fracture toughness of the investigated material
La Déformation Plastique Dynamique comme procédé monoétape d'élaboration pour l'optimisation des caractéristiques mécaniques des matériaux de structure : relations microstructure propriétés by Jérôme Mespoulet( )

1 edition published in 2020 in French and held by 1 WorldCat member library worldwide

Dans la famille des alliages de cuivre, le Cu - Be a longtemps été le matériau au compromis de performances conductivité électrique/résistance mécanique le plus élevé. Cependant, en raison de sa toxicité, l'utilisation du Béryllium est devenue contraignante. Des solutions de remplacement portent désormais sur d'autres nuances, de type Cu - Ti, Cu - Ni - Si ou encore Cu - Ni - Sn. Ces derniers n'ont cependant pas encore démontré pleinement leur équivalence. Ainsi, les présents travaux de thèse, qui se sont déroulés dans le cadre du développement de nouvelles microstructures pour répondre aux besoins constants de matériaux performants en conditions hautes pressions fluides (liquide en quasi statique ou gazeux en dynamique), ont permis d'évaluer la capacité du procédé d'élaboration en régime dynamique à élaborer, en une seule étape, des microstructures nouvelles et optimisées, par impact direct à des vitesses de 2250±50s-1 et 4250±50s-1.Les résultats obtenus permettent de dire que les premiers objectifs qui concernaient l'augmentation des propriétés mécaniques macroscopiques ont été atteints pour les deux alliages de l'étude, à savoir Cu - Be et Cu - Ni - Sn. En effet, des gains de ~28 et 23% par rapport aux états initiaux ont été obtenus sans recourir à des ajouts d'éléments d'addition rares, voire stratégiques pour lesquels le marché mondial est contraint (exemples : Ta, V, Nb...). Mieux, l'alliage Cu - Ni - Sn qui est appelé à remplacer, pour l'application envisagée, l'alliage Cu - Be a montré de réels espoirs, quant à sa stabilité microstructurale
 